N-14

Specification
AWS Specification: AWS A5.1 E6019
JIS Specification: D4301
Other Specification: 
Description
  • N-14 is an ilmenite type covered electrode for mild steel 
  • Excellent usability and mechanical properties
  • Good X-ray soundness 
  • Uniform slag-covering
  • Beautiful bead appearance
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

0.10

0.10

0.46

0.014

0.01

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

410  (60)

460 (67)

32

-18°, 80  (0°, 59)

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

2.6

3.2

4.0

5.0

LENGTH (mm)

350

350

350

350

Current Amp

Flat

55 - 90

85 - 140

130 - 190

180 -260

Vertical & Overhead

40 - 80

60 - 120

100 - 160

135 - 210


Welding Positions: ALL POSITIONS EXCEPT VERTICAL DOWN
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • For all position welding of heavy duty structures, such as ships, vehicles, building, and bridges made of mild steel.

 

  • If coating flux absorbs excessive moisture, arc and slag fluidity will become unstable resulting in increased spatters, undercuts, and blowholes
  • Damp electrodes should be re-dried at 70-120C for 60 minutes
  • Excessive high current and wide weaving deteriorate X-ray quality
  • Use optimum current and limit weaving width to within 2.5 times of the electrode diameter