N-6010

Specification
AWS Specification: AWS A5.1 E6010
JIS Specification: D4310
Other Specification: DIN E4343C4
Description
  • N-6010 is designed for all positions, providing deep penetration with a spray arc, flat bead, and thin brittle slag
  • Weld deposit has high tensile strength, ductility and is of X-ray quality
  • Excellent weldability in vertical and overhead positions
  • Deposition efficiency is higher than conventional types due to iron powder in the coating
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

0.10

0.20

0.50

0.013

0.012

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

420  (61)

500 (73)

27

-29°, 85  (-20°, 63)

 

SIZE AND RECOMMENDED CURRENT RANGE: DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

350

350

350

350

Current Amp

Flat & Vertical Down

50 - 80

80 - 110

100 – 150 

140 - 200

Vertical Up & Overhead

30 - 70

50 - 100

70 - 120

120 - 180


Welding Positions: ALL POSITIONS INCLUDING VERTICAL DOWN
Approvals: ABS

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Used primarily for storage tanks, ship-building, vehicles, pipes, galvanized plants, bridges, heavy equipment, building structure, etc. 
  • Use DC reverse polarity (DC+) current
  • Maintain a short to medium arc
  • Hold electrode perpendicularly to work surface and slightly inclined in direction of travel, keeping size of molten pool small
  • Clear each bead well before applying the next
  • Vertical welding can be done starting from the top or the bottom as the work requires
  • For overhead welding, best results are obtained by the multiple beads method
  • Dry the electrodes at 60-70C for 30 minutes before use