N-8016-G

Specification
AWS Specification: AWS A5.5 E8016G
JIS Specification: D5316
Other Specification: N/A
Description
  • N-8016-G is an extra low hydrogen type electrode for all position welding of 520 - 570 N/mm2 high tensile strength steel at low temperatures
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

Ni

0.08

0.50

1.28

0.012

0.010

0.62

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

530 (770)

640 (93)

29

-29°, 120  (-20°, 89)

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

350

350

350

350

Current Amp

Flat

55 - 85

90 - 130

135 - 185

190 - 250

Vertical & Overhead

50 - 80

80 - 120

110 - 160

165 - 210


Welding Positions: ALL POSITIONS 
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • For 520 - 570 N/mm2 high tensile strength steel welding of ships, machinery, and bridges
  • Dry the electrodes at 300 - 350C for 30-60 minutes before use
  • Take the backstep method or strike the arc on a small steel plate to prevent blowholes at the arc starting
  • Keep the arc as short as possible