NSF S.S. (FLUX) / NSAW-308L (WIRE)

Specification
AWS Specification: AWS A5.9 ER 308L
JIS Specification: N/A
Other Specification: N/A
Description
  • NSF-S.S. (FLUX) is an agglomerated bonded type flux for welding 18% Cr - 8% Ni (low carbon) stainless steel that features high desposition rate, high strength, and good bead appearance
  • NSAW-308L (WIRE) is a stainless welding wire that features balanced chromium and nickel levels, with low carbon content, for high resistance and reduced possibility of intergranular carbide precipitation
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Cr

Ni

Mo

0.03

0.48

1.67

19.22

9.77

-

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 

570 (83)

41

 

WIRE SIZES AVAILABLE:

DIAMETER (mm)

2.4

3.2

4.0

4.8


NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • For welding of low carbon 18% Cr - 8% Ni stainless steel
  • Wire Packing: 25 KG per coil
  • Flux Packing: 50 KG per sack