EZ-Ag35FC (COATED)

Specification
AWS Specification: AWS A5.8 BAg-2
JIS Specification: N/A
Other Specification: N/A
Description
  • EZ-Ag35FC (COATED) is a low temperature, economical, brazing filler metal capable of bridging gaps where tight joints fit-up cannot be maintained
  • Has a tendency to liquate (separate into low and high melting constituents) when heated slowly and therefore it is preferable to use it where the heat source is sufficient to raise the part temperature rapidly through the melting range of the brazing filler metal
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

Ag

Cu

Zn

Cd

Ni

P

35

26

21

18

-

-

 

TYPICAL MECHANICAL PROPERTIES:
Solidus
°C
Liquidus
°C
Density
KG/cm3
 

605

700

9.2

 

SIZE AVAILABLE: 
DIAMETER (mm)
1.6

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • For brazing silver-based alloys