FLUX CORED WIRE (FCAW)

NFCW-308LT-1

Specification
AWS Specification: AWS A5.22 E308LT1-1
JIS Specification: JIS Z3323 YF308LC
Other Specification: N/A
Description
  • NFCW-308LT-1 provides stable arc, easy slag removal, less spatter, and minimal welding fumes
  • Weld metal includes optimum ferrite contents in its austenitic structures
  • Features excellent weldability and low crack susceptibility
     
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

Ni Cr

0.03

0.62

1.56

0.022

0.010

10.50 19.50

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (kgf/mm2)
 
Tensile Strength
N/mm2 (kgf/mm2)
 
Elongation
%
 
Impact Value
J (kfg/m)
 

380 (30)

400 (58)

41

57 (5.8)

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+),

DIAMETER (mm)

2.6

3.2

4.0

5.0

LENGTH (mm)

350

350

350

350

Current Amp

Flat

50 - 80

70 - 110

120 – 160 

160 - 200

Vertical Overhead

40 - 70

60 - 100

110 - 150

140 - 180


Welding Positions: ALL POSITIONS INCLUDING VERTICAL DOWN
Approvals: ABS, BV, DNV, LRS, NK

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Weldability for all position welding includes vertical, overhead, and horizontal position
  • Excellent performance in automatic welding processes, such as robotic process
  • For welding of 18% Cr – 8% Ni stainless steel (SUS 304, SUS 304L)
  • Also suitable for MAG welding

about us

Industrial Welding Corporation (IWC) was established in 1982 by Mr. H. Ong Hai who had 25 years of welding industry experience (at that time). Since then, IWC has consistently and successfully earned an excellent ...

contact us

17 Mac Arthur Hi-way, Potrero, Malabon, Metro Manila, 1475 Philippines
(+632) 363-7865 / 66 / 68
(+632) 361-0255
(+632) 362-2668
sales@nihonweld.com
admin@nihonweld.com
export@nihonweld.com
Copyright © 2018 Industrial Welding Corporation Web Design By WebToGo Philippines