C |
Si |
Mn |
P |
S |
Diffusable Hydrogen Content (ml/100g) |
|
0.04 |
0.53 |
1.45 |
0.016 |
0.008 |
3.5 |
|
Yield Point
N/mm2
|
Tensile Strength
N/mm2
|
Elongation
%
|
Reduction Area %
|
Impact Value J at 0ºC, -20ºC |
|
510 |
570 |
27 |
69 |
100, 64 |
|
DIAMETER (mm) |
1.2 |
1.6 |
|
|
Current Amp |
Flat |
120 - 300 |
180 - 450 |
| Vertical Up & Overhead | 120 - 260 | 180 - 280 | |
|
Vertical Down |
200 - 300 |
250 - 300 |
|
|
Wire Diameter (mm) |
Welding Current (Amp) |
Nozzle Height (mm) |
Gas Flow Rate (l/min) |
|
1.2 |
100 - 200 |
10 - 15 |
15 - 25 |
| 200 - 300 | 15 - 25 | 20 - 30 | |
| 1.6 | 200 - 300 | 15 - 20 | 20 - 30 |
| 300 - 450 | 20 - 25 | 20 - 30 |
| Welding Positions: | ALL POSITIONS INCLUDING VERTICAL DOWN |
| Approvals: | N/A |
NOTE:
The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.