NSS-316L-17

Specification
AWS Specification: AWS A5.4 E316L-17
JIS Specification: N/A
Other Specification: N/A
Description
  • NSS-316L-17 is a lime-titania type stainless steel electrode that gives an extra low carbon
  • Spatter free
  • Deposited metal features excellent resistance to the intercrystalline corrosion due to extra low carbon content
  • Self-peeling slag

 

TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Ni

Cr

Mo Cu

0.02

0.65

0.84

12.30

19.30

2.42 0.03

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 

441  (64)

600 (87)

39

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

1.6

2.0 2.6

3.2

4.0

5.0

LENGTH (mm)

250

250 300

350

350

350

Current Amp

Flat

10 - 30

15 - 50 40 - 80

60 - 130

90 - 150

110 - 180

Vertical & Overhead

10 - 30

15 - 50 40 - 50

60 - 130

90 - 150

100 - 170


Welding Positions: ALL POSITIONS EXCEPT VERTICAL DOWN
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Used for welding corresponding steel grades, such as AISI 316 and 316L
  • Can also be used, under certain conditions, for welding ferritic-austenitic steel, such as AISI 329, 405, 410, and 430
  • Welding of titanium and nobium stabilized steels (e.g. 316Ti) in cases where the service temperature is below 400ºC
  • Widely used in various chemical industries
  • Clean off dust or oil from the welding area in order to prevent from decreasing the corrosion resistance caused by inter-blending carbon to the deposited metal