NSS-316L-15

Specification
AWS Specification: AWS A5.4 E316L-15
JIS Specification: D316L-15
Other Specification: N/A
Description
  • NSS-316L-15 is based on lime-titania formula and recommended for welding with DC (+) current
  • Welds are porosity free
  • Corrosion resistant
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

Ni

Cr

Mo

0.03

0.40

1.21

11.40

19.20

2.30

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 

590  (86)

39

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

2.5

3.2

4.0

5.0

LENGTH (mm)

300

350

350

350

Current Amp

Flat

50 - 80

70 - 110

100 - 150 

130 - 180

Vertical & Overhead

45 - 75

65 - 105

95 - 140

-


Welding Positions: ALL POSITIONS 
Approvals: N/A

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Welding of AISI types 316 and 316L stainless steel
  • Keep the arc length as short as possible
  • Keep welding current as low as possible

about us

Industrial Welding Corporation (IWC) was established in 1982 by Mr. H. Ong Hai who had 25 years of welding industry experience (at that time). Since then, IWC has consistently and successfully earned an excellent ...
Copyright © 2018 Industrial Welding Corporation
Web Design By WebToGo Philippines