N-7024

Specification
AWS Specification: AWS A5.1 E7024
JIS Specification: D5024
Other Specification: DN E5121RR11160
Description
  • N-7024 is a rutile coated high recovery manual metal arc electrode for the high speed welding of mild and medium tensile steels
  • Manufactured using a heavy coating containing a large proportion of iron powder giving a nominal efficiency of 160% 
  • Has a rapid melt-off rate and is suited to high productivity applications
  • Exhibits excellent welding operability with little spatter and trouble free strike and re-strike characteristics
  • Suitable for use in the flat position for butt welds and in the gravity and horizontal-vertical positions for fillet welds
  • Self detaching slag
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

0.08

0.40

0.72

0.020

0.010

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

505  (73)

560  (81)

27

0°, 70  (32°, 52)

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+), DC (-)

DIAMETER (mm)

3.2

4.0

5.0

LENGTH (mm)

350

450

450

Current Amp

Flat & Horizontal

130 - 180

180 - 220

240 - 290


Welding Positions: HORIZONTAL, FLAT
Approvals: ABS, BV, DNV, LRS

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Structural steel
  • Girders
  • Beams
  • Tanks
  • Vehicles 
  • Adjust the welding current to keep the proper slag covering because optimum welding current is subject to the welding process and the surface condition of steel plate
  • In the case of horizontal fillet welding, keep the optimum speed ratio among 1.0 ? 1.5
  • Dry the electrodes at 70 ? 100 C for 30 ? 60 minutes before use because excessive moisture absorption causes undercut and irregular beads