SHIELD METAL ARC WELDING (SMAW)

 Printer Friendly Layout

N-1300 WHITE

Specification
AWS Specification: AWS A5.1 E6013
JIS Specification: D4313
Other Specification: N/A
Description
  • N-1300 WHITE / RED is the most versatile general purpose rutile coated welding electrode for welding in all positions including vertical down
  • Easy initial arc strike ignition and "cold" re-striking (re-ignition) properties
  • Easy tack welding or point welding
  • Ultra smooth, quite, and stable arc
  • Reduced smoke and fumes during welding
  • Self-removing slag, which reduces cleaning and slag removing time
  • Beautiful and finely rippled bead for nice finishing and appearance
  • Can perform "touch type" or "contact" welding 
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

0.08

0.33

0.38

0.016

0.010

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

450  (65)

510 (74)

27

0°, 80  (32°, 59)

 

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

3.2

4.0

5.0

LENGTH (mm)

350

350

350

Current Amp

Flat & Vertical Down

100 - 130

130 - 180

170 - 230

Vertical Up & Overhead

90 - 120

120 - 170

160 - 220

Welding Positions: ALL POSITIONS INCLUDING VERTICAL DOWN
Approvals: ABS

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Steel structure, such as trusses, portal frames, tubed framework
  • Sheet and plate metal structures and containers (i.e. plating, storage tanks, hoppers, silos, bins)
  • Pipes for water, gas, and fluid transmission
  • Light steel frames (i.e. grills, ornamental and gate works, furniture)
  • General workshop and welding maintenance
  • Pay attention not to exceed the range of proper currents
  • Welding with excessive current not only lowers X-ray soundness, but also causes increase of spatter, under-cut, and insufficient slag covering
  • Dry the electrodes at 70-100 degrees C for 30-60 minutes before use
  • Excessive moisture absorption lowers usability and may result in porosity
  • Excessive drying before use causes less penetration and overheating of the electrode