N-13

Specification
AWS Specification: AWS A5.1 E6013
JIS Specification: D4313
Other Specification: N/A
Description
  • N-13 is a medium-thick coated rutile electrode for welding light and medium fabrications
  • Automatic striking and restriking properties
  • Beautiful, shiny, and smooth weld bead appearance
  • Touch type or contact welding feature
  • Self-removing slag
  • Minimum spatter
  • Soft and stable arc
TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

C

Si

Mn

P

S

0.07

0.32

0.41

0.012

0.010

 

TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
Yield Point
N/mm2 (KSI)
 
Tensile Strength
N/mm2 (KSI)
 
Elongation
%
 
Impact Value
°C, J (°F, Ft-Lbs)
 

430  (62)

480 (70)

28

0°, 65  (32°, 48)

SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

DIAMETER (mm)

3.2

4.0

5.0

LENGTH (mm)

350

400

400

Current Amp

Flat & Vertical Up

90 - 130

140 - 180

200 - 240

Vertical Down & Overhead

80 - 120

130 - 170

190 - 230


Welding Positions: ALL POSITIONS EXCEPT VERTICAL DOWN
Approvals: ABS

NOTE:

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

  • Steel structure trusses, portal frames, tubed framework
  • Sheet and plate metal structures (i.e. containers, storage tanks, hoppers, silos, and bins)
  • General steel fabrication and assembly job
  • Light steel frames (i.e. grills, ornamental and gate works, furniture)
  • General workshop welding and maintenance
  • Pay attention not to exceed the range of recommended currents
  • Welding with excessive current not only lowers X-ray soundness but also causes increase of spatter, under-cut, and insufficient slag covering
  • Dry the electrodes at 70-100°C for 30-60 minutes before use
  • Excessive moisture absorption lowers usability and may result in porosity
  • Excessive drying before use causes less penetration and overheating of the electrode
  • For Philippine market only

ABOUT US

For over 40 years, NIHONWELD has been the market leader of high quality welding electrodes in both the domestic and international markets. With Nihonweld, you will WELD WITH COMPLETE CONFIDENCE.
Copyright © 2018 Industrial Welding Corporation
Web Design By WebToGo Philippines