N-102

Specification

AWS Specification: AWS A5.1 E6013
JIS Specification: D4313
Other Specification: DIN E4342R(C)3

Description

Application

Remarks

  • Pay attention not to exceed the range of proper currents
  • Welding in excessive current increases spatter, undercut, and insufficient covering
  • Dry the electrodes at 70-100C for 30-60 minutes before use
  • Excessive moisture absorption lowers usability and may result in some porosity
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C

    Si

    Mn

    P

    S

    0.08

     

     

     

     

     

    0.15

    0.47

    0.014

    0.008

     

    TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
    Yield Point
    N/mm2 (KSI)
     
    Tensile Strength
    N/mm2 (KSI)
     
    Elongation
    %
     
    Impact Value
    °C, J (°F, Ft-Lbs)
     

    430  (62)

    470 (68)

    31

    0°, 120  (32°, 89)

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm)

    2.6

    3.2

    4.0

    5.0

    LENGTH (mm)

    350

    350

    350

    350

    Current Amp

    Flat

    50 - 100

    90 - 130

    140 - 180

    190 - 250

    Vertical Overhead

    50 - 90

    80 - 130

    110 - 170

    140 - 210


    Welding Positions: ALL POSITIONS
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.