N-CuAl-C

Specification

AWS Specification: AWS A5.6 ECuAl-C
JIS Specification: N/A
Other Specification: N/A

Description

Application

Remarks

  • Preheating is not necessary in the case of mild steels
  • Preheat at 250ºC - 300ºC in the case of welding brass
  • Keep the arc length as short as possible
  • Do not use too much weaving
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    Cu

    Al

    Fe

    Si

    Others

    Bal.

    12.0 - 13.0

    3.0 - 5.0

    1.00 max

    0.50 max

     

    TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
    Yield Point
    N/mm2 (KSI)
     
    Tensile Strength
    N/mm2 (KSI)
     
    Elongation
    %
     
    Hardness HB
     

    320 (46)

    620 (90)

    4

    200 - 210

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+), DC (-)

    DIAMETER (mm)

    3.2

    4.0

    5.0

    LENGTH (mm)

    350

    350

    350

    Current Amp

    70 - 110

    100 - 150

    140 - 180


    Welding Positions: FLAT, FILLET, VERTICAL UP, HORIZONTAL, OVERHEAD
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.