NHF-600B

Specification

AWS Specification: N/A
JIS Specification: DFA-600-R
Other Specification: DIN E2-60

Description

Application

Remarks

  • Preheat at 150ºC and over
  • In the case of multi-layer build-up welding or hardenable steel welding, underlay with low hydrogen type electrode (N-7016 or N-8016)
  • Dry the electrodes at 300-350ºC for 30-60 minutes before use
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C

    Si

    Mn

    Cr

    Mo

    0.65

    0.52

    0.43

    8.78

    5.03

     

    HARDNESS OF WELD METAL:
    Hardness
    Vickers (Hv)
    Rockwell (HRC)

    Value

    580 - 680

    54 - 58

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm)

    3.2

    4.0

    5.0

    LENGTH (mm)

    350

    350

    350

    Current Amp

    80 - 110

    100

    150 - 200


    Welding Positions: FLAT, FILLET, VERTICAL UP, HORIZONTAL, OVERHEAD
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.