N-6027

Specification

AWS Specification: AWS A5.1 E6027
JIS Specification: D4327
Other Specification: N/A

Description

Application

Remarks

  • Adjust the welding current to keep the proper slag covering because the optimum welding current is subject to the welding process and the surface condition of the steel plate
  • In the case of manual welding, operate by contact welding
  • In the case of gravity welding, the optimum speed ratio is 1.2-1.5
  • Dry the electrodes at 70-100 degrees C for 30-60 minutes before use
  • Excessive moisture absorption casuses undercuts and irregular beads
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C

    Si

    Mn

    P

    S

    0.07

    0.35

    0.71

    0.015

    0.011

     

    TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
    Yield Point
    N/mm2 (KSI)
     
    Tensile Strength
    N/mm2 (KSI)
     
    Elongation
    %
     
    Impact Value
    °C, J (°F, Ft-Lbs)
     

    430 (62)

    490 (71)

    31

    -29°, 67  (-20°, 49)

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm)

    3.2

    4.0

    5.0

    LENGTH (mm)

    450

    450

    450

    Current Amp

    Flat

    90 - 130

    120 - 180

    170 - 230

    Fillet

    80 - 120

    110 - 170

    160 - 220


    Welding Positions: FLAT, FILLET
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.