N-17

Specification

AWS Specification: AWS A5.1 E6019
JIS Specification: D4301
Other Specification: 

Description

Application

Remarks

  • If coating flux absorbs excessive moisture, arc and slag fluidity will become unstable resulting in increased spatters, undercuts, and blowholes
  • Damp electrodes should be re-dried at 70-120C for 60 minutes
  • Excessive high current and wide weaving deteriorate X-ray quality
  • Use optimum current and limit weaving width to within 2.5 times electrode diameter
  • Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C

    Si

    Mn

    P

    S

    0.09

    0.08

    0.61

    0.013

    0.01

     

    TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:
    Yield Point
    N/mm2 (KSI)
     
    Tensile Strength
    N/mm2 (KSI)
     
    Elongation
    %
     
    Impact Value
    °C, J (°F, Ft-Lbs)
     

    420  (61)

    470 (68)

    31

    -18°, 80  (0°, 66)

     

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm)

    2.6

    3.2

    4.0

    5.0

    LENGTH (mm)

    350

    350

    400

    400

    Current Amp

    Flat

    50 - 85

    80 - 130

    120 – 180 

    170 - 250

    Vertical & Overhead

    40 - 80

    60 - 110

    100 - 150

    130 - 200


    Welding Positions: ALL POSITIONS EXCEPT VERTICAL DOWN
    Approvals: N/A

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and test results for mechanical properties, deposit, or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design, and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.