AWS Specification: ER-80S-G
JIS Specification:

YGT-1CM

Other Specification:

DIN 17155 15Mo3 FOR CrMo STEEL

 

 

I. APPLICATIONS:

For welding of 1.25% Cr - 0.50% Mo steel.

 II. TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%): 

 

C

Si

Mn

Cr

Mo

0.07

0.52

1.01

1.24

0.54

III. TYPICAL MECHANICAL PROPERTIES OF WELD METAL :  

 

Tensile Strength N/mm2 (Ksi)

Yield Point

N/mm2 (Ksi)

Elongation %

Impact Value

°C,J (°F, Ft-Lbs)

630 (91)

540 (78)

28

, 270 (32°,199) 690°C x 1hr

 IV. SIZES AVAILABLE :

 

Dia.(mm)

1.6

2.0

2.4

3.2

4.0

Length (mm)

1000

1000

1000

1000

1000

Unit wt./packing (kgs.)

5.0

5.0

5.0

5.0

5.0

 

For welding of 1.25% Cr - 0.5% Mo steel.

 

TYPICAL ANALYSIS OF FILLER WIRE:

C

Si

Mn

Cr

Ni

Mo

S

P

 

0.07

0.52

1.01

1.24

-

0.54

0.005

 0.007

 

 

TYPICAL ALL WELD MECHANICAL PROPERTIES:

Yield Point

N/mm2 (Ksi)

Tensile Strength

N/mm2 (Ksi)

Elongation

%

Impact Value

Deg C, J (Deg F, Ft-lbs)

540 (78)

630 (91)

28

270 (32,199)

690degC x 1 hr

 

TIG DIAMETERS: 1.6, 2.0, 2.5, 3.2, 4.0 mm

TIG PACKING: 5KG per plastic container, 4 plastic containers per master carton box

 

MIG DIAMATERS: 0.6, 0.8 0.9, 1.0, 1.2, 1.6 mm

MIG PACKING: 15KG per spool, then placed in corrugated box

Small spool for 0.6 and 0.8mm available (6 Kg per spool)

 

TEST RESULT

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.