NIHONWELD N-NiMo-1
AWS Specification: ENiMo-1
JIS Specification:

NONE

Other Specification:

I. APPLICATIONS:

Welding of HASTELLOY B. Surfacing of the parts which needs corrosion resistibility against hydrochloric acid and sulphuric acid.

     II. DESCRIPTION:

   N-NiMo-1 produces HASTELLOY B weld whicis excellent for heat resistibility and corrosion resistibility. It is suitable for surfacing of the parts which is subjected to the attack of hydrochloric acid, sulphuric acid and nitric acid.

     III. NOTES ON USAGE:

  •       Preheating and postheating are unnecessary.
  • Weld with stringer bead.

  • Dry the electrodes at 150 ~ 200ºC for 30 ~ 60 minutes before use.

IV. TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%):

 

C

Si

Mn

Fe

Ni

Mo

V

0.02

0.30

0.76

5.91

Bal.

28.36

0.18

V. TYPICAL MECHANICAL PROPERTIES OF WELD METAL:

 

Tensile Strength

N/mm2 (ksi)

Elongation

%

Hardness

748 (109)

31

96 HRB

VI. WELDING POSITIONS: FLAT, FILLET, VERTICAL UP, HORIZONTAL, OVERHEAD

VII. SIZES AVAILABLE AND RECOMMENDED CURRENTS: AC/DC (+)

 

Size

(mm)

Dia.

3.2

4.0

5.0

Length

350

350

350

Current Range

Flat

70~110

100~150

130~180

Amp

Vertical & OH

65~105

95~140

-

 

 TEST RESULT

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.


 


 




 


 

 

 

 

 

 

which is excellent for heat resistibility and corrosion resistibility.  It is suitable for surfacing of the parts which is subjected to the attack of hydrochloric acid, sulphuric acid and nitric acid.

 

APPLICATIONS

            Welding of HASTELLOY B.  Surfacing of the parts which needs corrosion resistibility against hydrochloric acid and sulphuric acid.

 

INSTRUCTION FOR WELDING

(1)     Preheating and postheating are unnecessary.

(2)     Weld with stringer bead.

(3)     Dry the electrodes at 150 ~ 200ºC for 30 ~ 60 minutes before use.

 

TYPICAL ANALYSIS OF ALL WELD DEPOSIT:

C

Si

Mn

Fe

Ni

Mo

V

 

 

0.02

0.30

0.76

5.91

Bal

28.36

0.18

 

 

 

TYPICAL ALL WELD MECHANICAL PROPERTIES:

Yield Point

N/mm2 (Ksi)

Tensile Strength

N/mm2 (Ksi)

Elongation

%

HARDNESS

NA

748 (109)

31

96 HRB

 

RECCOMMENDED CURRENTS: Ampere (AC/DC+)

Size

Dia

3.2

4.0

5.0

(mm)

Length

350

350

350

Current

Range

Flat

70-110

100-150

130-180

Vertical & OH

65-105

95-140

-

 

WELDING POSITIONS:

FLAT, FILLET, VERTICAL UP, HORIZONTAL, OVERHEAD

 

Packing: in 5Kg plastic container, then 4 5kg containers in master carton box

Other special requests for packing such as plastic container ands vacuum packed plastics and even sealed steel cans can be accommodated.