nihonweldnihonweldnihonweld

Printer Friendly Layout
NIHONWELD N-8016-B1
AWS Specification: E8016-B1
JIS Specification:

NONE

Other Specification:

I. APPLICATIONS:

Welding of 0.5% Cr-0.5% Mo steel used for high temperature and high pressure boilers, chemical and oil refining industries.

 II. DESCRIPTIONS:

N-8016-B1 is a low hydrogen type electrode for all-position welding, which provides the weld metal 0.5% Cr-0.5% Mo. The crack is resistibility of the weld metal is excellent.

III. NOTES ON USAGE:

  • Dry the electrodes at 325-375ºC for about one hour before use.

  • Preheat at 125-250ºC and postheat at 620-680ºC.

  • Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blowholes at the arc starting.

  • Keep the arc as short as possible.

IV. TYPICAL CHEMICAL COMPOSITION OF DEPOSITED METAL (%):

 

C

Si

Mn

Cr

Mo

0.07

0.51

0.81

0.51

0.49

V. TYPICAL MECHANICAL PROPERTIES OF  DEPOSITED METAL

 

Tensile Strength N/mm2 (Ksi)

Yield Point N/mm2

(Ksi)

Elongation %

PWHT

670 (97)

590 (86)

26

690°C x 1hr.

VI.  WELDING POSITIONS : ALL POSITION EXCEPT VERTICAL DOWN

VII. SIZES & RECOMMENDED CURRENT RANGE: AC or DC (+)

 

Diameter (mm)

 

2.5

3.2

4.0

5.0

Length (mm)

 

350

350

400

400

Ampere

Flat

50 - 75

70 - 110

110 - 155

155 - 200

V & OH

30 - 70

55 - 105

90 - 140

 

 TEST RESULT

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.

 

 

 

 

.